Sains Malaysiana 44(4)(2015):
613–618
Understanding Pore Formation and Structural Deformation in
Carbon Spheres During KOH Activation
(Memahami Pembentukan Liang dan Penyahbentukan Struktur Sfera
Karbon Semasa Pengaktifan KOH)
M.S. MUSA1, M.M. SANAGI1,2*, H. NUR2 & W.A.WAN IBRAHIM1
1Department
of Chemistry, Faculty of Science, Universiti Teknologi Malaysia
81310
UTM Johor Bahru, Johor, Malaysia
2Ibnu
Sina Institute for Fundamental Science Studies, Nanotechnology Research
Alliance
Universiti
Teknologi Malaysia, 81310 UTM Johor Bahru, Johor, Malaysia
Diserahkan:
18 Ogos 2014/Diterima: 30 Oktober 2014
ABSTRACT
Carbon spheres (CSs) were synthesized from sucrose by
hydrothermal reaction. The synthesized materials were further activated with
potassium hydroxide (KOH) at different concentrations. The effects
of KOH concentration on the surface area and morphology were
investigated. The route for pore formation and structural deformation in carbon
spheres during activation has been proposed and discussed based on micrographs
and porosity trends. It was suggested that the pore formation and structural
deformation phenomena were due to the intercalating power of energized K+ into
the carbon. This work provides an insight of the pore formation in carbon spheres
for the development of adsorbents as well as for the understanding of the
structural deformation of such materials at higher KOH concentrations.
Keywords: Carbon spheres; hydrothermal reaction; KOH activation;
morphology; surface area
ABSTRAK
Sfera karbon (CSs) telah disintesis daripada sukrosa dengan
tindak balas hidroterma. Bahan yang telah disintesis telah diaktifkan dengan
kalium hidroksida (KOH) pada kepekatan berbeza. Kesan kepekatan KOH terhadap
luas permukaan dan morfologi telah dikaji. Laluan bagi pembentukan liang dan
penyahbentukan struktur sfera karbon semasa pengaktifan telah dicadang dan
dibincangkan berdasarkan mikrograf dan tren keliangan. Dicadangkan iaitu
fenomena pembentukan liang dan penyahbentukan struktur tersebut adalah disebabkan
oleh kuasa tujahan K+ yang bertenaga ke dalam karbon. Kerja ini memberikan
penerangan tentang pembentukan liang di dalam sfera karbon bagi pembangunan
bahan penjerap dan juga pemahaman tentang penyahbentukan struktur bahan
berkenaan pada kepekatan KOH yang tinggi.
Kata kunci: Luas permukaan; morfologi;
pengaktifan KOH; sfera karbon; tindak balas hidroterma
RUJUKAN
Deshmukh, A.A., Mhlanga, S.D. & Coville,
N.J. 2010. Carbon spheres. Material Science and Engineering Reports 70:
1-28.
Frykstrand, S., Forsgren, J., Mihranyan, A.
& Strømme, M. 2014. On the pore forming mechanism of Upsalite, a micro-and
mesoporous magnesium carbonate. Microporous and Mesoporous Materials 190:
99-104.
Hu, B., Yu, S., Wang, K., Liu, L. & Xu, X.
2008. Functional carbonaceous materials from hydrothermal carbonization of
biomass: An effective chemical process. Dalton Transactions 40:
5414-5423.
Inagaki, M. & Tanaike, O. 2001. Determining
factors for the intercalation into carbon materials from organic solutions. Carbon 39: 1083-1090.
Li, M., Li, W. & Liu, S. 2011. Hydrothermal
synthesis, characterization, and KOH activation of carbon spheres from glucose. Carbohydrate Research 346: 999-1004.
Lillo-Ro´Denas, M.A., Cazorla-Amoro´S, D. &
Linares-Solano, A. 2003. Understanding chemical reactions between carbons and
NaOH and KOH: An insight into the chemical activation mechanism. Carbon 41:
267-275.
Lowell, S., Shields, J.E., Thomas, M.A. &
Thommes, M. 2004. Characterization of Porous Solids and Powders: Surface
Area, Pore Size and Density. 4th ed. Dordrecht: Springer Publishers.
Lozano-Castello, D., Lillo-Ródenas, M.A.,
Cazorla-Amorós, D. & Linares-Solano, A. 2001. Preparation of activated
carbons from Spanish anthracite I. Activation by KOH. Carbon 39:
741-749.
Niwase, K., Homae, T., Nakamura, K.G. &
Kondo, K. 2002. Generation of giant carbon hollow spheres from C60 fullerene by
shock-compression. Chemical Physics Letters 362: 47-50.
Okuno,
H., Grivei, E., Fabry, F., Grunberger, T.M., Gonzalez- Aguilar, J.,
Palnichenko, A., Fulcheri, L., Probst, N. & Charlier, J.C. 2004. Synthesis
of carbon nanotubes and nano-necklaces by thermal plasma process. Carbon 42:
2543-2549.
Qian,
H., Han, F., Zhang, B., Guo, Y., Yue, J. & Peng, B. 2004. Non-catalytic CVD
preparation of carbon spheres with a specific size. Carbon 42: 761-766.
Qiao,
W.M., Song, Y., Lim, S.Y., Hong, S.H., Yoon, S.H., Mochida, I. & Imaoka, T.
2006. Carbon nanospheres produced in an arc-discharge process. Carbon 44:
187-190.
Raymundo-Piñero,
E., Azaïs, P., Cacciaguerra, T., Cazorla- Amorós, D., Linares-Solano, A. &
Béguin, F. 2005. KOH and NaOH activation mechanisms of multiwalled carbon
nanotubes with different structural organisation. Carbon 43: 786-795.
Sevilla,
M. & Fuertes, A.B. 2009. Chemical and structural properties of carbonaceous
products obtained by hydrothermal carbonizaon of saccharides. Chemistry A
European Journal 15(16): 4195-4203.
Wang,
Q., Li, H., Chen, L. & Huang, X. 2001. Monodispersed hard carbon spherules
with uniform nanopores. Carbon 39: 2211-2214.
*Pengarang untuk surat-menyurat; email: marsin@kimia.fs.utm.my
|
|||
|